Preparation and characterization of transparent TiO2 thin films coated on fused-silica substrates
學年 97
學期 1
出版（發表）日期 2009-01-01
作品名稱 Preparation and characterization of transparent TiO2 thin films coated on fused-silica substrates
作品名稱（其他語言）
著者 Yu, Hsuan-Fu; Hu, Fa-Chun
單位 淡江大學化學工程與材料工程學系
出版者 Secaucus: Springer New York LLC
著錄名稱、卷期、頁數 Journal of Sol-Gel Science and Technology 52(1), pp.158-165
摘要 The transparent TiO2 thin films coated on fused-SiO2 substrates were prepared by the sol–gel method and spin-coating technique. Effects of calcination temperature on crystal structure, grain size, surface texture, and light transmittance of the films were investigated. After calcining at 600–1,200 °C, the thicknesses of the TiO2 films were all around 80 nm and the molecular structures of the films were anatase, even at 1,200 °C. The calcined TiO2 films had the ultraviolet light (wavelength 200–400 nm) transmittances of ≦29% and the visible light (wavelength 400–800 nm) transmittance of ≧72%. By photocatalytically decomposing the methylene blue (MB) in water, the photocatalytic activities of the TiO2 thin films were measured and represented using the characteristic time constant (τ) for the MB degradation. While the films prepared at 1,000 and 1,200 °C photodecomposed about 54 mol% of the MB in water (the corresponding τ ≈ 14.8 h) after exposing to 365-nm UV light for 12 h, the films prepared at 600 and 800 °C had smaller s (≈ 9.0 h) and photodecomposed about 74 mol% of the MB in water at the same testing conditions.
關鍵字 Titanium oxide; Photocatalysis; Structural properties; X-ray diffraction; Thin films
語言 en
ISSN 0928-0707; 1573-4846
期刊性質 國外
收錄於 SCI EI
產學合作
通訊作者 Yu, Hsuan-Fu
審稿制度
國別 USA
公開徵稿
出版型式 紙本
相關連結

機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/53689 )

機構典藏連結