Diamagnetic and Electrical Properties of SixMo2S3−x (x = 0.1, 0.2, 0.33, 0.5) and A0.1Mo2S3−x (A = C, B, and Ru)
學年 101
學期 1
出版（發表）日期 2013-01-01
作品名稱 Diamagnetic and Electrical Properties of SixMo2S3−x (x = 0.1, 0.2, 0.33, 0.5) and A0.1Mo2S3−x (A = C, B, and Ru)
作品名稱（其他語言）
著者 Huang, G.T.; Chao, W.H.; Chang, J.K.; Liad, H.D.; Ling, D.C.; Chien, F.Z.; Wu, M. K.
單位 淡江大學物理學系
出版者 New York: Springer New York LLC
著錄名稱、卷期、頁數 Journal of Superconductivity and Novel Magnetism 26(3), pp.503–510
摘要 Mo2S3 doped with Si, C, B, and Ru, is identified to bear the same crystalline structure P21/m as that of Mo2S3 through XRD analysis. Diamagnetic transitions with χm ∼ 10−4 emu/gOe at temperature ranging from 2 K to 6 K were observed in the doped samples of SixMo2S3−x (x = 0.1, 0.2, 0.33, 0.5). And both of the x = 0.2 and 0.5 samples were found to have double diamagnetic transitions with higher Tc at the same temperature of 6.01 K, while SixMo2S3−x of x = 0.33 displayed an extra ferromagneticlike response at 63 K. The corresponding transition in resistivity of SixMo2S3−x with x = 0.1 was noticed to show a mild drop with less than 10%of its original transition values as measured down to 2 K. But a superconducting-like magnetic field dependence on the phase transition of resistivity was also noted. Its diamagnetic signals were greatly reduced when the applied magnetic fields were raised to 103 Oes. In the doped samples of A0.1Mo2S2.9 (A = C, B, and Ru), the phase transition in resistivity at 4.08 K, 4.62 K, and 4.35 K, respectively, exhibited similar fashion as that in the case of Si0.1Mo2S2.9.
關鍵字 SixMo2S3−x;Diamagnetic transition;Phase transition in resistivity
語言 en_US
ISSN 1557-1939 1557-1947
期刊性質 國外
收錄於 SCI EI
產學合作
通訊作者
審稿制度 是
國別 USA
公開徵稿
出版型式 紙本
相關連結

機構典藏連結 ( http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/85047 )

機構典藏連結